TC18鈦合金變形本構關系及其熱軋過程有限元仿真的應用Constitutive relationship and its application in finite element simulation of hot rolling of TC18 titanium alloy

基于熱模擬試驗，構建TC18合金的Arrhenius型材料本構關系，并將其應用于TC18板坯多道次軋制工藝的有限元仿真，獲得各道次軋制過程中的軋件溫度場、等效應力-應變場、損傷場等分布情況以及載荷-軋制時間狀態(tài)，進而為軋件尺寸預測以及軋機規(guī)格的選取提供指導。軋件每道次仿真所得尺寸與具體試驗所得尺寸比較可知，寬展誤差不超過0.7%，長度誤差不超過4%。經(jīng)四道次熱軋試驗后，在軋件邊緣1 mm區(qū)域出現(xiàn)了裂紋，與仿真所得損傷場分布一致。上述驗證表明仿真結果能夠與熱軋試驗較好吻合。

Based on thermal simulation a Arrhenius type constitutive relationship of TC18 titanium alloy was applied to the finite element simulation of multi-lane hot rolling. The field of temperature, stress-strain and damage and the load-time status at every lane were investigated to predict the rolling size and the specification of rolling mill. The error in spreading width and rolling length between simulating and experimental results are less than 0.7% and 4% at each lane, respectively. Crack occurs at 1 mm edge of the workpiece after four-lane hot rolling experiment, which is in accordance with the damage field obtained from simulation. The above verification shows that the simulation are coincident with the experimental results.

全文下載：http://pan.baidu.com/s/1kTthAXT