7050-T7452鍛件模擬高溫服役環(huán)境下組織性能的演化
發(fā)布人：上海艾荔艾金屬材料有限公司m.85978597.cn
更新時(shí)間：2015-08-24
通過(guò)拉伸試驗(yàn)和微觀組織觀察等方法對(duì)經(jīng)過(guò)不同溫度和時(shí)間模擬高溫服役環(huán)境熱暴露處理后7050-T7452鍛件的室溫拉伸性能以及合金金相組織、析出相的變化情況進(jìn)行系統(tǒng)研究。
7050-T7452鍛件模擬高溫服役環(huán)境下組織性能的演化Evolution of microstructure and properties of 7050-T7452
alloy forging simulation in high temperature service environment
通過(guò)拉伸試驗(yàn)和微觀組織觀察等方法對(duì)經(jīng)過(guò)不同溫度和時(shí)間模擬高溫服役環(huán)境熱暴露處理后7050-T7452鍛件的室溫拉伸性能以及合金金相組織、析出相的變化情況進(jìn)行系統(tǒng)研究。結(jié)果表明：7050-T7452鍛件在100~
175 ℃下熱暴露處理后，合金的強(qiáng)度隨熱暴露溫度的提高和時(shí)間的延長(zhǎng)而降低，伸長(zhǎng)率隨之增加；當(dāng)熱暴露溫度超過(guò)125
℃后，變化更為明顯；隨熱暴露溫度和時(shí)間的變化，合金的晶粒尺寸以及再結(jié)晶程度沒(méi)有明顯改變；當(dāng)熱暴露溫度≤125
℃時(shí)，合金晶粒內(nèi)部析出相的尺寸和種類沒(méi)有明顯變化；隨熱暴露時(shí)間的增加，晶界無(wú)析出帶的寬度略有增寬；當(dāng)熱暴露溫度超過(guò)125
℃時(shí)，合金晶內(nèi)的析出相隨溫度以及熱暴露時(shí)間的增加而迅速粗化，η相的體積分?jǐn)?shù)增加，晶界無(wú)析出帶加寬，合金的強(qiáng)度明顯下降。
The evolution of microstructure and properties of
7050-T7452 alloy forging simulation in high temperature service environment for
different times and temperatures was studied by tensile test and transmission
electron microscopy．The results show that the strength of 7050-T7452 alloy
forging decreases with the thermal exposed time and temperature increasing in
the range of 100-175 ℃, however, the elongation increases. The change of
strength is obvious when the exposed temperature is higher than 125 ℃, and the
change of grain size and recrystallization is not obvious. When the exposed
temperature is lower than 125 ℃, the sizes and species of precipitates do not
change obviously. The width of precipitate-free zones (PFZs) increases a little
with the exposed time increasing. When the exposed temperature is higher than
125 ℃, the precipitates in matrix are coarser with the exposed temperature and
time increasing. Meanwhile, the precipitate size and width of PFZs increase
obviously, and the dominant precipitate is η phase. The strength of alloy
decreases visibly in this period.