2197鋁鋰合金形變熱處理中T1相的析出行為
發(fā)布人：上海艾荔艾金屬材料有限公司m.85978597.cn
更新時(shí)間：2015-09-28
對(duì)2197鋁鋰合金進(jìn)行形變熱處理，采用HREM高分辨電鏡觀察合金欠時(shí)效和峰時(shí)效兩個(gè)階段的顯微組織，研究T1相析出長(zhǎng)大行為及其界面特征。
2197鋁鋰合金形變熱處理中T1相的析出行為Precipitation behavior of T1 phase duringthermo-mechanical treatment of 2197 Al-Li alloy
對(duì)2197鋁鋰合金進(jìn)行形變熱處理，采用HREM高分辨電鏡觀察合金欠時(shí)效和峰時(shí)效兩個(gè)階段的顯微組織，研究T1相析出長(zhǎng)大行為及其界面特征。結(jié)果表明：形變熱處理2197合金在欠時(shí)效階段主要存在δ′、θ′和T1相，T1相尺寸約為40 nm；峰時(shí)效階段合金中δ′和θ′數(shù)量減少，主要析出相為T1相，其尺寸為50~150 nm，T1相可通過(guò)δ′相的溶解而長(zhǎng)大。在欠時(shí)效和峰時(shí)效兩階段，T1相末端與基體共格，其他區(qū)域與基體非共格。T1相為六方晶系，與基體存在慣析關(guān)系：(0001)T1//(111)A1、[1010]T1//[110]A1，慣析面為{111}A1。
2197 Al-Li alloy was thermo-mechanically treated, and the precipitation and growth of the T1 phase and the phase interface characteristics were studied. The microstructures of thermo-mechanical treated 2197 Al-Li alloy for under-aged and peak-aged states were observed by high resolution electron microscopy (HREM). The results show that during thermo-mechanical treatment, δ′, θ′ and T1 phases are the main phases of under-aged 2197 alloy, the size of T1 phase is about 40 nm. δ′ and θ′ phases number reduce at peak-aged state, while the main phase of peak-aged 2197 alloy is T1 phase with the size of 50-150 nm. The T1 phase grows up by the dissolving of δ′ phase. The end of T1 phase of peak-aged 2197 alloy is coherent with the matrix while the rest is non-coherent during under-aged and peak-aged states. Habit relationships between T1 phase which is hexagonal crystal system and the matrix is as follow: (0001)T1//(111)A1?and [1010]T1//[110]?A1, and the habit plane is {111}A1.
以上資料由上海艾荔艾金屬材料有限公司提供，歡迎新老客戶來(lái)電洽購(gòu)。
本文來(lái)自上海艾荔艾金屬材料有限公司http://m.85978597.cn，轉(zhuǎn)載請(qǐng)注明出處。
前一頁(yè)：焊后熱處理對(duì)Al-Mg-Si-Cu合金激光焊接接頭微觀結(jié)構(gòu)和力學(xué)性能的影響
后一頁(yè)：內(nèi)高壓成形制備6063鋁合金異形管件的壁厚分布及尺寸精度