GH4169合金δ相的溶解行為及對變形機制的影響
發(fā)布人：上海艾荔艾金屬材料有限公司m.85978597.cn
更新時間：2015-11-02
采用光學(xué)顯微鏡(OM)、掃描電鏡(SEM)、電子背散射衍射(EBSD)技術(shù)和透射電鏡(TEM)研究GH4169合金中δ相在高溫變形條件下的演變規(guī)律，分析δ相的溶解過程及其動力學(xué)機制，探討δ相對GH4169合金高溫變形動態(tài)再結(jié)晶機制的影響。
GH4169合金δ相的溶解行為及對變形機制的影響Dissolution behavior of δ phase and its effects on?deformation mechanism of GH4169 alloy
采用光學(xué)顯微鏡(OM)、掃描電鏡(SEM)、電子背散射衍射(EBSD)技術(shù)和透射電鏡(TEM)研究GH4169合金中δ相在高溫變形條件下的演變規(guī)律，分析δ相的溶解過程及其動力學(xué)機制，探討δ相對GH4169合金高溫變形動態(tài)再結(jié)晶機制的影響。結(jié)果表明：隨變形溫度的升高或應(yīng)變速率的降低δ相含量減少，動態(tài)再結(jié)晶晶粒尺雨和體積含量增大，δ相主要以彎曲、扭折和切斷等方式來協(xié)調(diào)塑性變形，并在界面能降低的驅(qū)動力下由針狀逐漸轉(zhuǎn)變?yōu)槎提槧钅酥燎驙?；在高溫變形條件下，δ相的溶解時間大大縮短，位錯、空位和曲率對δ相的溶解起到重要作用，這主要與其對溶質(zhì)原子擴散行為的影響有關(guān)，變形過程中產(chǎn)生的大量高密度位借及空位為溶質(zhì)原子提供了眾多高速率擴散通道，促進(jìn)了δ相的溶解；δ相的存在改變了GH4169合金的動態(tài)再結(jié)晶機制，其動態(tài)再結(jié)晶機制主要有δ相誘發(fā)動態(tài)再結(jié)晶形核和非連續(xù)動態(tài)再結(jié)晶形核。
The evolution of δ phase during hot deformation of GH4169 alloy was investigated by optical microscopy (OM), electron backscattering diffractometry (EBSD), scanning and transmitting electron microscopy. The dissolution processes of δ phase and dynamic mechanisms were analyzed. The effect of δ phase on the mechanism of dynamic recrystallization (DRX) was discussed. The results show that, with increasing deformation temperature and decreasing strain rate, the content of δ phase decreases, but the grain size and volume fraction for dynamic recrystallization increase. The plastic deformation is mainly accommodated by bending, kinking and shearing of δ phase. Under the drive force of reduced interface energy, δ phase is transformed from needle to short needle and even sphere. The accelerated dissolution of δ phase can be attributed to the effect of dislocation, vacancy and curvature, which is concerned with the diffusion behavior of solute atoms. A larger amount of high-speed channels for the diffusion of solute atoms form due to the existence of massive defects, such as high density dislocations and vacancies, promoting the dissolution of δ phase. The main nucleation mechanisms of DRX are changed to be δ phase stimulated nucleation and discontinuous nucleation due to δ phase.
以上資料由上海艾荔艾金屬材料有限公司提供，歡迎新老客戶來電洽購。
本文來自上海艾荔艾金屬材料有限公司http://m.85978597.cn，轉(zhuǎn)載請注明出處。