真空去應力退火對TC18鈦合金殘余應力及組織性能的影響
發(fā)布人：上海艾荔艾金屬材料有限公司m.85978597.cn
更新時間：2015-12-16
在不同溫度和時間下對TC18鈦合金進行真空去應力退火處理，研究TC18鈦合金真空去應力退火前后力學性能及殘余應力的變化規(guī)律，觀察去應力退火后的金相組織和拉伸斷口形貌。
真空去應力退火對TC18鈦合金殘余應力及組織性能的影響Influence of vacuum stress relieving annealing on residual stress and microstructure properties of TC18 titanium alloy
在不同溫度和時間下對TC18鈦合金進行真空去應力退火處理，研究TC18鈦合金真空去應力退火前后力學性能及殘余應力的變化規(guī)律，觀察去應力退火后的金相組織和拉伸斷口形貌。結果表明：經真空去應力退火后，TC18鈦合金的抗拉強度和屈服強度降低，沖擊韌性、斷裂韌性、伸長率和斷面收縮率提高；殘余應力消除效果顯著；隨著退火溫度的升高，合金顯微組織呈現(xiàn)規(guī)律性變化；當溫度達到650 ℃以上時，α相明顯減少，亞穩(wěn)定β相顯著增加，導致其強度下降，與力學性能測試結果相吻合；合金塑性提高，與斷口形貌分析一致；最后，得到TC18鈦合金的真空去應力退火制度為600~650 ℃和1~4 h。
The different temperature and time parameters were adopted in the vacuum stress relieving annealing processes of TC18 titanium alloy. The evolution of mechanical properties and residual stress was researched, the microstructures and SEM images of fracture surfaces were also observed. The results show that, after the vacuum stress relieving annealing, the tensile and yield strengths of TC18 titanium alloy decrease, while the charpy toughness, fracture toughness, elongation and area reduction increase. The removing effect of residual stress is remarkable. Along with the increases of the temperature of stress relieving annealing, the microstructure of the alloy changes regularly. When the temperature exceeds 650 ℃, α-phase decreases obviously, and the metastable β-phase increases dramatically. Thus, the strength of the alloy decreases, which coincides with the result of mechanical properties. Meanwhile, the plasticity increases, which coincides with the fracture appearance. Finally, the vacuum stress relieving annealing schedule is obtained to be 600?650 ℃ and 1?4 h.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發(fā)電子郵件kefu@ailiaigroup.com聯(lián)系我們，您也可以通過微博和微信和我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo?and?Weixin.