SAE1141H鋼花鍵軸熱處理后開裂原因分析
發(fā)布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新時間：2016-04-30
用顯微組織觀察和超聲波探傷等方法，分析研究了SAE1141H鋼花鍵軸經(jīng)中頻感應(yīng)加熱淬火后檢驗時在線切割取樣過程中出現(xiàn)的開裂現(xiàn)象。
SAE1141H鋼花鍵軸熱處理后開裂原因分析Crack reason analysis on SAE1141H steel spline shaft after heat treatment用顯微組織觀察和超聲波探傷等方法，分析研究了SAE1141H鋼花鍵軸經(jīng)中頻感應(yīng)加熱淬火后檢驗時在線切割取樣過程中出現(xiàn)的開裂現(xiàn)象。結(jié)果表明，花鍵軸內(nèi)部并沒有裂紋，這種開裂是中頻感應(yīng)加熱淬火后花鍵軸中的殘余應(yīng)力在切割過程中釋放的結(jié)果，它起源于硫化物的偏聚區(qū)并沿著硫化物擴展。通過改變檢驗時取樣的切割路線可以有效避免這種開裂現(xiàn)象。
Cracks on SAE1141H free-cuRing steel spline shaft．occurred during linear cutting samples for check after medium—frequency?induction hardening，were analyzed with observation of microstructure and supersonic inspection etc．The results show that there are actually?no crocks inside of the shaft and the cracks are caused by the release of residual stress during sampling after medium·frequency induction?hardening．The cracks originate from the accumulation zone of sulphides and propagate along with the sulphides．It Can be effectively avoided?by changing the cutting route during sampling.
作為值得信賴的合作伙伴和高品質(zhì)金屬合金的半成品供應(yīng)商，艾荔艾擁有完善的服務(wù)體系和專業(yè)的團隊。在同客戶交易的過程中，我們力求根據(jù)不同的應(yīng)用需求將我們的產(chǎn)品做到精益求精。針對當(dāng)前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應(yīng)的合金和服務(wù)信息，請致電086-021-67660801或發(fā)電子郵件kefu@ailiaigroup.com聯(lián)系我們，您也可以通過微博，微信，領(lǐng)英，XING，臉書和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn,?XING, Facebook?and?Twitter.